--- type: "Article" title: "Comparative study of two XPS weld passivation processes" description: "Case study XPS weld passivation processes Comparative analysis of two methods of weld passivation using XPS spectroscopy Accueil • Blog • XPS weld passivation processes The problem? As part of a change in methodology, one of our clients wishes to..." resource: "https://filab.fr/en/blog/2025/12/comparative-study-of-two-xps-weld-passivation-processes/" tags: ["Analytical Techniques", "Case study", "EN", "pll_691d90ee146f2"] timestamp: "2026-01-22T13:18:34Z" published: "2025-12-02T07:05:17Z" language: "en" author: "bwa" --- # Comparative study of two XPS weld passivation processes Case study # XPS weld passivation processes Comparative analysis of two methods of weld passivation using XPS spectroscopy [Home](https://filab.fr) • [News](https://filab.fr/?post_type=post) • XPS weld passivation processes ## The problem? **As part of a change in methodology, one of our clients wishes to verify the effectiveness of a new passivation process in comparison with the old one. The percentage of oxidation of the iron and chromium elements is analyzed for each sample. The contribution of oxidized species within the oxygen element is also observed.** In order to carry out this study, FILAB developed an analytical approach using X-ray Photoelectron Spectroscopy (XPS) to perform an elemental, structural, and quantitative analysis of the extreme surface (a few nm deep) of a sample. ## Summary 01 Comparison of surface passivation processes using XPS [](#cont-01) 02 Study of the passivation depth of the two types of processes using XPS [](#cont-02) 03 Conclusion of the comparative study [](#cont-03) 01 ## Comparison of surface passivation processes using XPS **Objective :** The objective of this study is to verify the effectiveness of a new passivation process (paste, Sample 2) in comparison with the old one (bath, Sample 1). - The quantification and oxidation state of iron and chromium elements are characterized for each sample. - The contribution of oxidized species within the oxygen element is also observed. **Approach :** ![](https://filab.fr/wp-content/uploads/2025/03/passivation-def-300x169.gif) The study of the effectiveness of the two passivation processes for 316L stainless steel TIG welds is based on a nanoscale surface analysis using FILAB's analytical equipment. For this passivation study, FILAB drew on its dual expertise in materials and chemistry to determine the elemental composition of the 316L stainless steel TIG welds. Here, an XPS spectroscopy study of the two passivation processes (paste and bath) determined that the outer surface of the two samples has essentially the same elemental composition. In fact, they are composed mainly of oxygen, as well as iron and chromium. Other elements present in trace amounts are also observed. **Results :** XPS analysis therefore indicate that the surfaces of the two samples are well passivated. They also seem to indicate that these passivations are equivalent in terms of surface area. 02 ## Study of the passivation depth of the two types of processes using XPS **Objective:** Create a profile of the evolution of elemental concentrations present on the **surface** and **at depth** using several successive pulverizations through precise bombardment for each sample. **Approach :** The XPS analysis previously performed on the surface were repeated after each spraying process. The profiles of the evolution of the elemental composition according to depth in the sample for both processes were obtained. The following results were obtained. **Results :** ![NF EN 10088](https://filab.fr/wp-content/uploads/2023/12/acier-inoxydable-2-300x240.png) Despite very similar passivation quality on the surface, the two processes appear to produce different passivation thicknesses. Sample 2 (paste) has a thicker passivation layer (~15 nm vs. 8 nm for sample 1=bath), indicating better resistance to oxidation. Higher chromium concentration in sample 2 (17-18% versus 10%), suggesting a difference in the composition or treatment of the material. Oxygen diffusion is greater in sample 1, whereas it is severely limited at depth in sample 2. 03 ## Conclusion of the comparative study The XPS spectroscopy analysis carried out as part of this comparative study yielded the following information: - XPS analysis indicate that the surfaces of the two samples are well passivated. - XPS analysis seem to indicate that these passivation layers are equivalent on the surface. However, XPS profiles showed that the sample passivated with paste (new passivation) had a passivation layer three times thicker than the sample passivated with bath (old passivation). The diffusion of oxygen into the metal matrix beyond this passivation layer is also greater for the second sample. **The newly developed passivation process, involving the application of a paste, therefore appears to be better because it is thicker.** Need help? Contact our team [](#filab-contact-form) ## Other case studies you may be interested in ### [Learn more +](https://filab.fr/en/blog/2026/05/microplastics-detection-industrial-filters.md) ### Yellowing of silicone Silicones are now widely used in various fields thanks to their remarkable physical and chemical properties, such as excellent thermal stability, high resistance to oxidation and hydrolysis, and excellent gas permeability. [Learn more +](https://filab.fr/en/blog/2025/12/how-filab-helped-one-of-its-customers-understand-the-yellowing-phenomenon-of-a-silicone.md) ### Chromium oxidation Chromium is a chemical element belonging to the transition metals group. It is a hard, shiny, corrosion-resistant metal used in many fields due to its physical and chemical properties. Chromium has different oxidation states. [Learn more +](https://filab.fr/en/blog/2025/12/determination-of-chromium-oxidation-states-using-xps-case-study.md) [View all our case studies](https://filab.fr/en/blog-filab.md) ## Services related to the case study [## Metal analysis in black mass](https://filab.fr/en/metal-analysis-in-black-mass.md) [![avis filab](https://filab.fr/wp-content/themes/astra-child/templates/assets/img/avis-verifies.svg) 5/5 ![note filab](https://filab.fr/wp-content/themes/astra-child/templates/assets/img/stars.svg)](https://www.avis-verifies.com/avis-clients/filab.fr) ## Laboratory specializing in analysis and expertise for industrial companies ![More than 140 people](https://filab.fr/wp-content/uploads/2024/10/collaborateurs-1.svg) More than 140 people at your service ![5200 m² laboratory](https://filab.fr/wp-content/uploads/2024/10/labo.svg) 5200 m² laboratory + 99% of services are provided in-house ![Accredited laboratory](https://filab.fr/wp-content/uploads/2024/10/ISO-17025-1.svg) Accredited laboratory COFRAC ISO 17025 ![+2200 clients](https://filab.fr/wp-content/uploads/2024/10/clients.svg) +2200 clients in France and abroad ### Contact us Our services are reserved for professionals. [![phone](https://filab.fr/wp-content/themes/astra-child/templates/assets/img/form/phone.svg) Call us +33 (0)3 80 52 32 05](tel:+33380523205) [![location](https://filab.fr/wp-content/themes/astra-child/templates/assets/img/form/location.svg) Visit us 80 rue Jean-Louis Auguste Petitjean 21850 - Saint Apollinaire - FRANCE](https://www.google.com/maps/place/Filab/@47.317329,5.076545,15z/data=!4m6!3m5!1s0x47f29e6ab37d6a1d:0xa2cc1016c4f74422!8m2!3d47.317793!4d5.0767354!16s%2Fg%2F1v3gr7f0?entry=ttu) [![mail](https://filab.fr/wp-content/themes/astra-child/templates/assets/img/form/envelope.svg) Contact us contact@filab.fr](mailto:contact@filab.fr?subject=%5BVotre%20demande%20:%20Determination%20of%20chromium%20oxidation%20states%20using%20XPS%20-%20Case%20study%20en%20%5D) For complaints: all complaints must be sent by mail to contact@filab.fr or by contacting the person who signed the report. The complaint handling procedure is available upon request. In the event of a complaint concerning the laboratory's activities, the customer may be notified of the complaint's handling.